Provenance of Source Code

Etienne Girault,
Department MTM,
K.U. Leuven,
de Croylaan 2
3001 Leuven,

Top | Next


Normalised kinetics of isothermal bainite transformation at 416°C for a steel of composition: Fe-0.11C-1.50Si-1.53Mn-0.008P-0.006S-0.043Sol.Al-0.035 wt.% after intercritically annealing at 750°C for 1 min, 4 mins or 1 hour.

Top | Next | Prev


Heat treatment:
Intercritically annealed at 750°C for 1 minute, 4 minutes or 1 hour and then cooled at a rate between 75 and 100°C.s to isothermal bainite temperature of 416°C.

This was carried out in a Theta dilatometer using 15 x 4 x 0.8 mm flat specimen, using same equipment and steel as in reference [1].

This distribution consists of two files: bainnorm.txt is an ASCII text version of this document; bainnorm.dat is an ASCII text file containing the data, formatted as follows:

Column 1: 1 minute time / s
Column 2: 1 minute normalised bainite / %
Column 3: 4 minutes time / s
Column 4: 4 minutes normalised bainite / %
Column 5: 1 hour time / s
Column 6: 1 hour normalised bainite / %

Top | Next | Prev


  1. Jacques, P., Girault, E., Van Humbeeck, J., Aernoudt, E. and Delannay, F. (1997): IV European Symposium on Martensitic Transformations (Esomat '97), Enschede, The Netherlands, July 1997, in press.

Top | Next | Prev

Further Comments


Top | Next | Prev


materials, data, kinetics, isothermal, bainite, transformation, steel

Top | Next | Prev

Download data

Download data library

Top | Prev

MAP originated from a joint project of the National Physical Laboratory and the University of Cambridge.

MAP Website administration / map@msm.cam.ac.uk

Top | Library Index | MAP Homepage

Valid HTML 3.2!